System Three T-88 EPOXY


For well over 25 years T-88 has been the most widely used structural adhesive for
marine and general woodworking use in the United States.

•  Mix at a 1:1 by volume ratio.
• T-88 will cure at temperatures as low as 35ºF.
• Full Cure @ 77°F (25°C) 72 Hours
• When fully cured, it is unaffected by water, oil, kerosene, and many other chemicals.
• It will not stain wood and is immune to fungus and rot.
• T-88 is unique in that it may be applied to damp wood, provided it is worked well into the surface.


T-88 PHYSICAL PROPERTIES

Mix Ratio by Volume ..... 100:100
Mix Ratio by Weight ..... 100:83
Total Solids ..... 100%
Mixed Viscosity ..... 9,000 cps
Tensile Strength, psi ..... 7,000
Flexural Strength, psi ..... 11,500
Lap-Shear Strength, psi: ..... Polyester Laminate: 2,800
Concrete: ..... 1,100
Wood (Maple): ..... 1,800
Aluminum: ..... 2,000
Galvanized Steel: ..... 1,800
Copper: 1,650
Lap-Shear Strength vs. Temperature (Aluminum Tensile Shear) psi:  .....
67°F: ..... 2,500
75 °F: ..... 2,000
150°F: ..... 1,300
180°F: ..... 1,000
Heat Deflection Temperature ..... 119°F (49°C)
Maximum Service Temperature ..... 160°F (71°C)
Minimum Application Temperature ..... 35°F (2°C)
Coverage @ 20mils ..... 80 ft2/gal (2 m2/L)
Gel Time @ 77°F (25°C) ..... 60 Minutes (100g mixture)
Full Cure @ 77°F (25°C) ..... 72 Hours


Please enter quantities of desired items below then click

T88.8  -  System Three T88 EPOXY - 8 oz (1/2 Pint) Kit  -  $20.60  -  Quantity   
T88.16  -  System Three T88 EPOXY - 16 oz (One Pint) Kit  -  $32.95  -  Quantity   

Please enter quantities of desired items above then click


 

paypal_logo_reflect.png